核壳结构纳米铝粉热学行为

推进技术 ›› 2012, Vol. 33 ›› Issue (3): 478-482.

核壳结构纳米铝粉热学行为

郭连贵,宋武林,谢长生,胡木林

华中科技大学材料学院/模具技术国家重点实验室,湖北武汉 430074;江西蓝天学院材料研究与应用技术研究所,江西南昌 330098;华中科技大学材料学院/模具技术国家重点实验室,湖北武汉 430074;华中科技大学材料学院/模具技术国家重点实验室,湖北武汉 430074;华中科技大学材料学院/模具技术国家重点实验室,湖北武汉 430074

发布日期:2021-08-15
作者简介:郭连贵(1978—),男,博士,讲师,研究领域为新型能源材料的制备及其应用。E-mail:whglg@126.com
基金资助:
国家自然科学基金(51071073)。

Thermal Behavior of Core-Shell Structure Aluminum Nanopowders

State Key Laboratory of Dies Technology, Department of Materials Science and Engineering, Huazhong University of Science and Technology, Wuhan 430074, China;Institute of Material Research and Application Technology, Jiangxi Blue Sky University, Nanchang 330098, China;State Key Laboratory of Dies Technology, Department of Materials Science and Engineering, Huazhong University of Science and Technology, Wuhan 430074, China;State Key Laboratory of Dies Technology, Department of Materials Science and Engineering, Huazhong University of Science and Technology, Wuhan 430074, China;State Key Laboratory of Dies Technology, Department of Materials Science and Engineering, Huazhong University of Science and Technology, Wuhan 430074, China

Published:2021-08-15

摘要/Abstract

摘要： 为了研究不同表面包覆物对纳米铝粉热学行为的影响,采用激光-感应复合加热法制备了三种不同表面包覆的核/壳结构纳米铝粉(氧化铝钝化、碳包覆及增塑剂DOS包覆)。采用高分辨透射电镜(HRTEM)对制备的纳米粉末结构进行表征,并采用差示扫描量热及热重分析(DSC-TG)对不同物质包覆纳米铝粉的热学性能进行研究。结果表明,这些纳米粒子均呈现出明显的核壳结构,且包覆层厚度约3.5nm。这三种不同表面包覆纳米铝粉在400℃至铝熔点(660℃)之间均发生了氧化,但非氧化物包覆纳米铝粉(碳包覆与增塑剂DOS包覆)的氧化开始温度及峰温比氧化铝钝化纳米铝粉提前了约30℃左右,而且氧化放热热焓和氧化质量增重均高于氧化铝钝化纳米铝粉,表明这两种非氧化物表面包覆对纳米铝粉的热学行为有积极的影响。最后对不同物质包覆纳米铝粉的破壳氧化机制进行了探讨。

关键词: 含能材料;纳米铝粉;核壳结构;热学行为

Abstract: To discuss the effect of different surface coatings on the thermal behavior of Al nanopowders, three kinds of core-shell structure Al nanopowders with different surface coatings (Al₂O₃ passivation coating, carbon coating, and Plasticizer DOS coating) were prepared by laser-induction complex heating technology. The structure characterization of the as-prepared nanopowders was revealed using high resolution transmission electronic microscopy (HRTEM), and the thermal properties were investigated using differential scanning calorimeter (DSC) and thermal gravimeter (TG) analysis. The results show that these Al nanoparticles all show obvious core-shell structue, and the coating thickness is about 3.5 nm. The early oxidation of the three Al nanopowders with different surface coatings is observed between ~400 ℃ and the melting point of Al (~660 ℃). However, the onset temperature and the peak temperature for the oxidation of Al nanopowders with non-oxide protective coatings (carbon coating and Plasticizer DOS coating) are about 30 ℃ lower than those of Al₂O₃-passivated Al nanopowders, and the enthalpy change and the mass gain of them are higher than those of Al₂O₃-passivated Al nanopowders, which indicate that the two non-oxide surface coatings have a positive impact on the thermal behavior of Al nanopowders. The oxidation mechanism of broken shell of Al nanopowders with different surface coatings is discussed. 

Key words: Energetic materials; Aluminum nanopowders; Core-shell structure; Thermal behavior

郭连贵,宋武林,谢长生,胡木林. 核壳结构纳米铝粉热学行为[J]. 推进技术, 2012, 33(3): 478-482.

参考文献

[2] Kuo K K, Risha G A, Evans B J, et al.Potential Usage of Energetic Nano-Sized Powders for Combustion and Rocket Propulsion [J].Materials Research Society Symposium Proceedings, 4,0:3-14.
[3] Pantoya M L, Granier J J.Combustion Behavior of Highly Energetic Thermites:Nano Versus Micron Composites [J].Propellants, Explosives, Pyrotechnics, 5,0 (1):53-62.
[4] Kwon Y S, Gromov A A, Ilyin A P.Reactivity of Superfine Aluminum Powders Stabilized by Aluminum Diboride [J].Combustion and Flame, 2,1:349-352.
[5] Foley T J, Johnson C E,Higa K T.Inhibition of Oxide Formation on Aluminum Nanoparticles by Transition Metal Coating [J].Chemistry of Materials, 5,7(16):4086-4091.
[6] Jouet R J, Warren A D, Rosenberg D M, et al.Surface Passivation of Bare Aluminum Nanoparticles Using Perfluoroalkyl Carboxylic Acids [J].Chemistry of Materials, 5,7(11):2987-2996.
[7] Gromov A A, Ilyin A, Forter-Barth U, et al.Characterization of Aluminum Powders:Ⅱ.Aluminum Nanopowders Passivated by Non-Inert Coatings [J].Propellants, Explosives, Pyrotechnics, 6,1(5):401-409.
[8] 张凯, 傅强, 范敬辉,等.纳米铝粉微胶囊的制备及表征[J].含能材料,5,3(1):4-6.
[9] 谢长生, 胡木林, 胡军辉,等.激光感应复合加热制备金属纳米粉体材料[J].材料热处理学报, 1,2(1):20-23.
[10] 张小塔, 宋武林, 郭连贵,等.激光-感应复合加热法制备碳包覆纳米铝粉[J].推进技术, 7,8(3):333-336.(ZHANG Xiao-ta, SONG Wu-lin, GUO Lian-gui, et al.Preparation of Carbon-Coated Al Nanopowders by Laser-Induction Complex Heating method [J].Journal of Propulsion Technology, 7,8(3):333-336.)
[11] Guo L G, Song W L, Xie C S, et al.Characterization and Thermal Properties of Carbon-Coated Aluminum Nanopowders Prepared by Laser-Induction Complex Heating in Methane [J].Material Letters, 7,1:3211-3214.
[12] Guo L G, Song W L, Hu M L, et al.Preparation and Reactivity of Aluminum Nanopowders Coated by Hydroxyl-Terminated Polybutadiene (HTPB) [J].Applied Surface Science, 8,4:2413-2417.
[13] Kwok Q S M, Fouchard R C, Turcotte A M, et al.Charact-Erization of Aluminum Nanopowder Compositions [J].Propellants, Explosives, Pyrotechnics, 2,7(4).
[14] Ma Y W, Hu Z, Yu L S, et al.Chemical Functionalization of Magnetic Carbon Encapsulated Nanoparticles Based on Acid Oxidation [J].Journal of Physical Chemistry B, 6,0(41):20118-20122.
[15] Rai A, Lee D, Park K, et al.Importance of Phase Change of Aluminum in Oxidation of Aluminum Nanoparticles [J].Journal of Physical Chemistry B, 4,8(39):14793-14795.
[16] Bystrzejewski M, Cudzilo S, Huczko A, et al.Carbon Encapsulated Magnetic Nanoparticles for Biomedical Applications:Thermal Stability Studies [J].Biomolecular Engineering, 7,4:555-558.