推进技术 ›› 1994, Vol. 15 ›› Issue (6): 88-92.

• • 上一篇    下一篇

国产HTPB复合推进剂裂纹扩展特性的实验研究

屈文忠   

  1. 西安二炮工程学院
  • 发布日期:2021-08-15

EXPERIMENTAL RESEARCH ON CRACK GROWTH BEHAVIOR IN HTPB COMPOSITE PROPELLANT

  1. The Second Artillery Engineering College, Xi’an, 710025
  • Published:2021-08-15

摘要: 依据SchaperyRA[1]的粘弹性断裂理论,对国产HTPB复合推进剂进行了I型型纹扩展实验。分析了裂纹扩展的特性,表明裂纹扩展开始时存在临界应力强度因子KIC.得出了该型推进剂裂纹扩展速率da/dt与应力强度因子KI间的幂函数关系式。讨论了该推进剂材料断裂能与裂纹扩展速率的关系。

关键词: 端羟基聚了二烯推进剂;裂纹扩展;应力强度因子;应力试验

Abstract: In this paper, guided by Schapery’s theory of viscoelastic fracture, a model crack growth experiment was conducted with of HTPB composite propellant.Crack growth behavior was analyzed, showing that at the beginning of crack growth the critical stness intensity factor KIC exists. The power functional relationship of this propellant between crack growth rate da/dt and stress intensity factor KI was determined. The relationship between the fracture energy of this propellant and crack growth rate was discussed.

Key words: Hydroxy terminated polybutadiene propellant;Crack propagation;Stress intensity factor;Stress test