Abstract: Inordertoimprovetheignitionandcombustioncharacteristicsofaluminum/icefuels，theigni.tionandcombustioncharacteristicsofaluminum/icefuelswithdifferentmagnesiumpowdercontentswerestud.ied.Thecombustiontemperaturewasobtainedusingthermocoupleandtheburningphenomenawererecordedus.ingahigh-speedcamera.Theresultsshowedthataluminium/icefuelsappearedobviousoxidationexothermicre.actionat100～200℃withtheadditionofmagnesiumpowder.Theadditionofmagnesiumpowdercouldreducetheinitialreactiontemperatureofaluminum/icefuelsandacceleratethereactionofaluminumandice.Inthesta.blecombustionstage，combustionintensitydecreasedwithincreasingmagnesiumpowdercontents.Theanalysisofthecombustionproductsfoundthatmagnesiumpowderhadanobviousinfluenceonthemorphologyofcombus.tionproducts.Moreover，thecombustionofaluminum/icebasedfuelswasincomplete.

Key words: Fuel；Aluminum/Icefuels；Magnesiumpowder；Combustioncharacteristics

摘要： 为改善铝/冰燃料的点火燃烧性能，通过添加不同比例的镁粉制备成铝/冰基燃料，研究其对铝/冰燃料燃烧特性的影响。实验通过接触法测得铝/冰基燃料燃烧温度并采用高速摄影系统观测其燃烧现象。研究结果表明，铝/冰燃料中添加镁粉后在100～200℃即出现较为明显的氧化放热反应，镁粉可以明显降低铝/冰基燃料的起始反应温度，加快反应速率。在稳定燃烧阶段，随着镁粉添加量的增加，铝/冰基燃料燃烧剧烈程度降低。通过对燃烧产物的分析发现，添加镁粉后的燃烧产物形貌与未添加镁粉的产物形貌存在明显差别，且未完全反应的铝粉含量较多，燃烧相对不充分。

关键词: 燃料；铝/冰；镁粉；燃烧特性中图分类号:V512文献标识码:A文章编号:1001-4055(2015)12-1901-08DOI:10.13675/j.cnki.tjjs.2015.12.021